李亚楠
,
何迪
,
李树索
,
韩雅芳
金属学报
对Ni3Al基单晶合金IC6sx的表面进行吹砂变形处理; 再在800—1260℃热暴露1—10 h, 采用OM, SEM和EPM研究了IC6sx合金的再结晶行为. 结果表明, 合金再结晶开始形核的温度约1000 ℃, 一次再结晶完成的温度为1200—1210℃. 在1200—1240℃热暴露时的再结晶层厚度约为10 m, 而在1260 ℃热暴露时增长到约23 m. 再结晶在枝晶干长大的速度明显小于枝晶间, 再结晶层和基体的枝晶干之间观察到一种由粗大条状γ'相和γ+γ'相构成的胞状转变结构, 这是由于枝晶干中粗大的γ'相阻碍再结晶向基体内生长形成的.
关键词:
Ni3Al
,
single crystal alloy
,
recrystallization
,
null
Yanan Li Yafang Han
材料科学技术（英）
The recrystallization behavior of Ni3Al base single crystal alloy IC6SX with different mechanical processes has been studied.The specimens of the alloy were treated by surface cleaning and cold working during the blades manufacture, and then heat treated in the temperature range of 800{1260°C for 1 h to 4 h. The microstrcture of the specimens were examined by optical and scaning electron microscopy, and the room temperature tensile property, stress rupture property under the test condition of 1100°C/130 MPa, and the thermal cycle fatigue resistance under 1100−20°C of the specimens with and without recrystallization were carried out. The experimental results showed that the initial recrystallization nucleation temperatures of the alloy by dry grit blasting, wet grit blasting, indentation, shot blasting and burnishing were 900−950°C/1 h, 1000−1100°C/1 h,
1200−1220°C/4 h, 1220−1240°C/1 h and 1220−1240°C/1 h, respectively and the primal recrystallization completing temperatures of the alloy by those mechanical processes mentioned above were 1200−1210°C/1 h, 1100−1200°C/1 h, 1220−1240°C/4 h, 1240−1260°C/1 h and 1240−1260°C/1 h, respectively. The results also indicated that the deformation amount of the specimens by burnishing and dry grit blasting was bigger than that by wet grit blasting and shot blasting according to their recrystallization emperature and the micro-hardness profile below the surface of specimens. It has been found that the recrystallization had no evident effect on mechanical properties of the alloy.
关键词:
Ni3Al
,
single crystal alloy
,
recrystallization
,
surface layer
张静华
,
唐亚俊
,
张志亚
,
于洋
,
张济山
,
李英敖
,
胡壮麒
材料研究学报
本文研究一种在热腐蚀环境下工作的Ni 基单晶高温合金错配度以及γ′筏状形成与性能的关系;通过蠕变和持久试验,研究合金的变形组织和强化特点。在变形过程中,基体运动位错遇γ′相受阻而在γ′相表面形成位错网络,这种位错结构在变形中形成了新的强化机制,提高了合金的蠕变抗力。
关键词:
Ni基高温合金
,
single crystal alloy
,
dislocation structure
,
strengthening mechanism
罗兴宏
,
晋冬艳
,
任玉虎
中国材料进展
doi:10.7502/j.issn.1674-3962.2017.04.03
单晶合金由于没有晶界缺陷而具有特殊的理化性能,如镍基单晶高温合金是先进航空航天发动机和燃气涡轮发动机关键材料,具有优异的高温使役性能.单晶合金的特色结构决定了它只能通过凝固的方式获得,因而凝固过程对单晶合金的组织结构、成分分布乃至理化性能具有难以磨灭的影响.如以枝晶结构为主要特征的单晶合金中的枝晶结构参数、合金元素的宏观与微观偏析都与凝固过程参数(如凝固速度、温度梯度等)密切相关.研究表明,重力导致的各项效应(如浮力对流、沉降和流体静压等)直接或间接地影响凝固过程参数,并且是导致成分偏析和凝固缺陷的重要原因.但在常规地面条件下由于无法有效去除重力影响,因而难以清晰揭示凝固过程中的重力效应及其作用规律.而在微重力环境中,这一难题将迎刃而解.因此,近些年来国内外一些学者利用空间或模拟微重力环境,对重力对单晶凝固行为的影响及其在缺陷形成中的作用进行了研究.这些研究对于获得良好的单晶凝固组织、避免凝固缺陷的形成,以及提高单晶合金的质量和性能都有着重要的意义.综述了目前国内外微重力下单晶生长研究的相关进展,并对未来研究进行了展望.
关键词:
空间
,
微重力
,
单晶合金
,
晶体生长
,
凝固
,
缺陷